Pass the API ICP Programs API-571 Questions and answers with ExamsMirror

API RP 571 provides detailed insights:

“Brittle fracture generally occurs at low temperatures, specifically below the ductile-to-brittle transition temperature as defined by the Charpy impact test.”

“Most carbon and low-alloy steels are ductile above their Charpy transition temperature but may fracture suddenly without ductility below it.”

(Reference: API RP 571, Section 4.2.1.2 – Brittle Fracture)

Hence, option C is correct and technically accurate based on the material behavior curve.

From API RP 571, brittle fracture prevention measures include:

“Postweld Heat Treatment (PWHT) reduces residual stresses in the heat affected zone and base metal, thus lowering susceptibility to brittle fracture.”

“PWHT is particularly effective when applied to pressure-containing components fabricated from carbon steel or low-alloy steel that will experience low-temperature service.”

(Reference: API RP 571, Section 4.2.1.2 – Brittle Fracture)

Therefore, while other measures may reduce stress or detect flaws, PWHT directly targets one of the root causes: residual stress. Thus, option D is the best prevention method.

API RP 571 notes that for detecting existing cracks or flaws that may lead to brittle fracture, especially those that initiate at welds or surface stress points:

“Wet fluorescent magnetic-particle inspection is highly effective for detecting surface-breaking flaws in ferromagnetic materials that are susceptible to brittle fracture.”

“It is sensitive to tight cracks and surface discontinuities that may serve as initiation sites for brittle fracture.”

(Reference: API RP 571, Section 4.2.1.2 – Brittle Fracture)

Therefore, option A is correct as it is the most effective NDE technique for detecting early signs of brittle cracking.

API RP 571 and RP 939-C define sulfidation conditions as:

“Sulfidation of iron-based alloys generally becomes significant at temperatures above 500°F (260°C) in hydrocarbon streams with sulfur but without hydrogen.”

“For hydrogen-containing environments, this threshold may be reduced to 450°F (230°C).”

(Reference: API RP 571, Section 4.2.1.1 – Sulfidation; API RP 939-C, Section 3.1)

Therefore, the correct answer is D.

According to API RP 571 Section 5.1.3.4 (Naphthenic Acid Corrosion - NAC):

“Sulfur can act as an inhibitor to NAC. Where sulfur content in crude is high, a reduction in naphthenic acid corrosion is sometimes observed, especially in certain parts of vacuum and atmospheric units. However, this is not universally reliable, and corrosion can still occur based on local operating conditions and metal temperatures.”

Thus, Option C (Inhibition) is the correct choice, as sulfur can reduce NAC under some conditions.

From API RP 571 on Microbiologically Influenced Corrosion (MIC):

“MIC depends on the presence of water, nutrients, and specific microbial species such as SRB (sulfate-reducing bacteria).”

“While flow velocity may influence deposition and oxygen content, MIC can occur in both stagnant and flowing systems. Hence, it's not strongly dependent on velocity.”

Thus, option D is correct — MIC is largely independent of flow velocity.

According to API RP 571:

“Oxidation is the reaction of metal and oxygen to form oxides. It generally occurs in high temperature environments with excess oxygen.”

“Sulfidation is a high temperature corrosion mechanism that occurs due to interaction between sulfur-containing compounds and metal surfaces, forming metal sulfides. Like oxidation, sulfidation occurs in environments above 500 °F (260 °C).”

“Both oxidation and sulfidation can occur concurrently, particularly in mixed environments of oxygen and sulfur.”

(Reference: API RP 571, Sections 5.1.1 and 5.1.3 – Oxidation & Sulfidation)

These two mechanisms are thermally activated and occur in elevated temperature conditions found in heaters, furnaces, and piping systems. Hence, option B is correct.

From API RP 571 Section 5.3.3.2 (Caustic Corrosion):

“Caustic corrosion, also known as caustic gouging, occurs in boiler systems when caustic concentrates in under-deposit areas or due to improper steam drum and boiler water design. Good design and water treatment practices are key preventive measures.”

Temperature control or acid injection are not practical or effective mitigation techniques. Design considerations—such as proper water flow, material selection, and minimizing deposits—are essential.

Hence, the correct answer is Option C.

API RP 571 notes in the context of Hydrochloric Acid Corrosion in overhead condensers:

“Titanium is highly resistant to low pH acidic aqueous phases, including hydrochloric acid formed during condensation in overhead systems.”

“Stainless steels like 316 and 410 are not suitable in the presence of free chlorides at low pH and elevated temperatures.”

(Reference: API RP 571, Section 4.3.3.3 – Hydrochloric Acid Corrosion)

Thus, Titanium is the preferred alloy under the described acidic and high-temperature conditions, making option B correct.

API RP 571 states under Chloride Stress Corrosion Cracking (Cl-SCC):

“Nickel contents above approximately 35% provide significant resistance to chloride stress corrosion cracking. Alloys such as Alloy 625 and Alloy 825 exhibit excellent resistance.”

“Austenitic stainless steels with lower nickel contents, such as 304 and 316, are more susceptible to Cl-SCC.”

Hence, option C (35%) is correct.